4*0.5MM ASTM A254 DC 04 Galvanized/Zinc Coated Lowe Carbon Steel Bundy Coil Tube

The low carbon steel brake tube is supplied in single wall and double wall(Bundy Pipe). The products conform to ASTM A-254-91, A-512-91A, ASTM A214 and A513 in material and quality. Commonly sizes we supply to the client include 4.76mm×0.7 mm,6.35 mm×0.7 mm and 8 mm×0.7 mm.

Single wall steel tubing is the most common type of tubing used in household refrigeration applications. Bundy single wall tubing is manufactured by continuously forming a single low carbon steel strip into a tubular shape and welding the adjoining edges using a high-frequency induction welding process. Through strict process controls, the internal weld bead is held to a minimum and all external flashing is removed. Corrosion-resistant coatings are applied inline to assure uniform coverage.

SINGLE WALL STEEL TUBING OD & WT TOLERANCE

All the tube diameters can be available plain, zinc-coated or copper coated.

PLAIN TUBE

The plain tube is supplied with its outside surface slightly oiled to improve the resistance to oxidation. The tube shall be kept in dry storages, away from air drafts, humidity or any other corrosive agents

ELECTROLYTIC BOTH SIDE COPPER COATING

The steel strip from which the tube is made shall be copper coated on both sides with a copper layer ≥2µm. The area along the welding seam, on the outside surface is not coated because of the scarfing operation to remove the excessive bead.

HOT DIP ZINC COATING

Tube outside surface can be coated with a layer of zinc whose weight is ≥ 70 grams per square meter determined by UNI EN ISO 1460/97. This coating the tube withstands to > 72 h in salt spray fog test before showing red rust (according to UNI ISO 9227).