ASTM A254 SPCC 4.76*0.6MM Electro-welded Single Wall Refrigeration Zinc-coated Steel Bundy Tubing

It is mainly used on refrigeration condenser and evaporator, brake tube, oil injection tube line and link pipe parts. It would be in coils and straight tubes.

Single-Wall Steel Tubing with the same coating range as double-wall tubing but with the addition of a nickel-coated internal diameter to withstand the corrosive environment created by modern-day fuels.

Production Standard :ASTM A269, ASTM A249,ASTM A554,ASTM A312,DIN17457,DIN17455,EN10217

Single wall steel tubing is the most common type of tubing used in household refrigeration applications. Bundy single wall tubing is manufactured by continuously forming a single low carbon steel strip into a tubular shape and welding the adjoining edges using a high-frequency induction welding process. Through strict process controls, the internal weld bead is held to a minimum and all external flashing is removed. Corrosion-resistant coatings are applied inline to assure uniform coverage.

SINGLE WALL STEEL TUBING OD & WT TOLERANCE

All the tube diameters can be available plain, zinc-coated or copper coated.

PLAIN TUBE

Plain tube is supplied with its outside surface slightly oiled to improve the resistance to oxidation. Tube shall be kept in dry storages, away from air drafts, humidity or any other corrosive agents

ELECTROLYTIC BOTH SIDE COPPER COATING

The steel strip from which the tube is made shall be copper coated on both sides with a copper layer ≥2µm. The area along the welding seam, on the outside surface is not coated because of the scarfing operation to remove the excessive bead.

HOT DIP ZINC COATING

The tube outside surface can be coated with a layer of zinc whose weight is ≥ 70 grams per square meter determined by UNI EN ISO 1460/97. This coating the tube withstands to > 72 h in salt spray fog test before showing red rust (according to UNI ISO 9227).

WORKING SHOP

Laboratory Testing Equipment

PACKING