Contacts：Miss. Lisa
0086-13861277353
Contacts：Miss. Lisa
0086-13861277353
Contacts：Miss. Lisa
Tel：0086-13861277353
E-mail：linsa188@gmail.com
Add：No.143 Qingyang North road,Tianning district. Changzhou
| Place of Origin: | Changzhou |
| Brand Name: | Joyruns |
| Certification: | ISO9001 |
| Model Number: | 25.4*2.77 |
| Minimum Order Quantity: | 2Tons |
| Price: | |
| Packaging Details: | plastic packing, end caps, wooden box packing |
| Delivery Time: | 30days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 2000Tons/Month |
|
Detail Information |
|||
| Product Name: | ASTM A334 Carbon Steel Pipe | OD Size: | 6mm To 114.3mm |
|---|---|---|---|
| Thickness: | 1mm To 20mm | Standard: | DIN2391, EN10305, EN10216, EN10210. ASTM A334 |
| Material: | ST35, ST45, ST52.Gr.6.Gr.1 | Type: | Seamless Cold Drawning Precision Tube |
| Delivery State: | +N, +NBK,+C,+BKS,+GBK | ||
| High Light: | ST45 Low Temperature Carbon Steel Pipe,DIN2391 Low Temperature Carbon Steel Pipe,ST35 Seamless Alloy Steel Pipes |
||
ASTM A334 Gr.6 low-temperature seamless tube
ASTM A334 Carbon Steel Pipe brief introduction
The usage of the ASTM A334 GR.6 Carbon Steel Pipe is seen in petrochemical industries, marine industries, food processing plants and in the oil and gas industries.
ASTM A334/A334M specification covers several grades of minimum wall-thickness, seamless and welded, carbon and alloy-steel tubes intended for use at low temperatures. Some product sizes may not be available under this specification because heavier wall thicknesses have an adverse effect on low-temperature impact properties.
Manufacture: the tubes shall be made by the seamless process and shall be either hot-finished or cold-finished, as specified.
Heat Treatment: all seamless tubes shall be treated to control their microstructure in accordance with one of the following methods:
a: Normalize by heating to a uniform temperature of not less than 1550 °F [845 °C] and cool in the air or in the cooling chamber of an atmosphere-controlled furnace.
b: Reheat and control hot working and the temperature of the hot-finishing operation to a finishing temperature range from 1550 to 1750 °F [845 to 955°C] and cool in a controlled atmosphere furnace from an initial temperature of not less than 1550 °F [845 °C].
Inspection & Test: chemistry composition analysis, tension test, flattening test, flaring test, hardness test, impact test, NDT, surface inspection and dimension check.
|
C, % |
Mn, % |
Si, % |
P, % |
S, % |
|
0.30 max |
0.29-1.06 |
0.10 min |
0.025 max |
0.025 max |
|
Tensile Strength, MPa |
Yield Strength, MPa |
Elongation, % |
Hardness, HB |
|
415 min |
240 min |
30 min |
190 max |
| Cold Drawn | Outside Diameter, mm | Tolerance, mm |
| OD＜25.4 | ±0.10 | |
| 25.4≤OD≤38.1 | ±0.15 | |
| 38.1＜OD＜50.8 | ±0.20 | |
| 50.8≤OD＜63.5 | ±0.25 | |
| 63.5≤OD＜76.2 | ±0.30 | |
| 76.2≤OD≤101.6 | ±0.38 | |
| 101.6＜OD≤190.5 | +0.38/-0.64 | |
| 190.5＜OD≤228.6 | +0.38/-1.14 |
Wall thickness & Tolerance
| Cold Drawn | Outside Diameter, mm | Tolerance, % |
| OD≤38.1 | +20/-0 | |
| OD>38.1 | +22/-0 |